UHMW-PE Fender pads and fenders are produced by a sintering process either from virgin or from reclaimed material (aprox. 70% reclaimed +30% virgin material - also named double-sintered or blended UHMW-PE).
UHMW-PE (UltraHighMolecularWeight-PolyEthylene) combines highest strength with wear resistance and consequently provides the best durabilty of all available Polyethylene products.
Advantages are:
● Very high impact strength
● Very low friction coefficient
● Very high abrasion resistance
● UV + Ozone resistant
● Non-conducting (optional)
● 100% recycable, non-rottening
● Cut to size sheet ,all size is available with us
● Standard colour :Black ,Yellow ,Blue ,Green ,Red,White ,other colour is available upon request .
The application is as follows:
● low resistance sliding plates on fender panels
● low resistance slinding panels for bridge and pier protection
● corner protection for offshore structures, berths and other marine facilities
Specification (For special requirements ,please contact us):
| Item | Test method | Unit | UHMWPE 1000-V | UHMWPE 1000-DS |
| Density | ISO1183-1 | g/cm3 | 0.93-0.95 | 0.95-0.96 |
| Yield Strength | ASTM D-638 | N/mm2 | 15-22 | 15-22 |
| Breaking Elongation | ISO527 | % | undefined200% | undefined100% |
| Impact strength | ISO179 | Kj/m2 | 130-170 | 90-130 |
| Abrasion | ISO15527 | Steel=100 | 80-110 | 110-130 |
| Shore Hardness | ISO 868 | Shore D | 63-64 | 63-67 |
| Friction Coefficient(Static state) | ASTM D-1894 | Unitless | undefined0.2 | undefined0.2 |
| Operating temperature | - | ℃ | -80 to +80 | -80 to +80 |
UHMW-PE Flat Fender pad ,UHMW-PE Corner Fender pad ,UHMW-PE Edge Fender pad all is available:
For special drawing and properties of UHMW-PE Fender facings /UHMW-PE Fender pad ,please contact us by our email.